offers extended functionality!CAMPUS® datasheet | ORGALLOY LE 60LMXV
This datasheet of ORGALLOY LE 60LMXV from ARKEMA is provided by the international plastics database CAMPUS.
CAMPUS is organized by a group of leading international resin producers, who have agreed to test their material according to uniform conditions, based on ISO standards (ISO 10350, ISO 11403), in order to offer comparable data to the market.
ORGALLOY LE 60LMXV | PA6... | ARKEMA
Product Texts
ORGALLOY LE 60LMXV LE series, flexible polyamide alloys: processability on PE screw, low moisture absorption, chemical resistance (no known solvents). The grades referenced: lower in rigidity than LE 6000 (900 MPa). See also : LE 60LM (750 MPa). Suited to the extrusion of tubes (hydraulic, pneumatic, painting ...)
| Rheological properties | dry / cond | Unit | Test Standard |
| Melt volume-flow rate (MVR) | 4 / * | cm³/10min | ISO 1133 |
| Temperature | 235 / * | °C | ISO 1133 |
| Load | 2.16 / * | kg | ISO 1133 |
| Mechanical properties | dry / cond | Unit | Test Standard |
| Tensile Modulus | - / 600 | MPa | ISO 527-1/-2 |
| Yield stress | - / 30 | MPa | ISO 527-1/-2 |
| Yield strain | - / 7 | % | ISO 527-1/-2 |
| Nominal strain at break | - / >50 | % | ISO 527-1/-2 |
| Charpy impact strength (+23°C) | - / N | kJ/m² | ISO 179/1eU |
| Charpy notched impact strength (+23°C) | - / N | kJ/m² | ISO 179/1eA |
| Thermal properties | dry / cond | Unit | Test Standard |
| Melting temperature (10°C/min) | 220 / * | °C | ISO 11357-1/-3 |
| Vicat softening temperature (50°C/h 50N) | 60 / * | °C | ISO 306 |
| Burning Behav. at 1.5 mm nom. thickn. | HB / * | class | IEC 60695-11-10 |
| Thickness tested | 1.6 / * | mm | IEC 60695-11-10 |
| Burning Behav. at thickness h | HB / * | class | IEC 60695-11-10 |
| Thickness tested | 3.2 / * | mm | IEC 60695-11-10 |
| Electrical properties | dry / cond | Unit | Test Standard |
| Comparative tracking index | * / 600 | - | IEC 60112 |
| Other properties | dry / cond | Unit | Test Standard |
| Water absorption | 5.5 / * | % | Sim. to ISO 62 |
| Humidity absorption | 1.5 / * | % | Sim. to ISO 62 |
| Density | 1030 / 1030 | kg/m³ | ISO 1183 |
| Test specimen production | Value | Unit | Test Standard |
| Injection Molding, melt temperature | 260 | °C | ISO 294 |
| Injection Molding, mold temperature | 60 | °C | ISO 10724 |
Diagrams
Characteristics
Processing
Injection Molding, Profile Extrusion, Other Extrusion, Transfer Molding
Delivery form
Pellets
Additives
Plasticizer
Special Characteristics
Platable, Light stabilized or stable to light, Heat stabilized or stable to heat
Regional Availability
Other text information
Injection molding
PREPROCESSING
Max water content: 0,05-0,15 %
Notice text : ORGALLOY grades are delivered ready for use.
: If Orgalloy is not used within 4 hours of opening
: the bag,the product should be redried at 90°C
: during 4 hours.
PROCESSING
Melt temperature : 240-280 °C
Mold temperature : 20- 60 °C
Notice text : To avoid degradation, it is recommended to limit
: injection moulding temperature to 300°C.
: A higher mould temperature leads to higher shrinkage..
POSTPROCESSING
Annealing
-Temperature : 80-120 °C
-Time : 0,5 - 1 h
Notice text : Post treatment enables optimum dimensional
: stability.The treatment temperature is function
: of the temperature towhich the part will experience.
: ORGALLOY grades have low sensitivity to humidity.
: Therefore it is not normally necessary to
: precondition prior to assembly.
Profile extrusion
PREPROCESSING
Max water content: 0,05-0,15 %
Notice text : ORGALLOY grades are delivered ready for use.
: If Orgalloy is not used within 4 hours of opening
: the bag,the product should be redried at 90°C
: during 4 hours.
PROCESSING
Melt temperature : 255-265 °C
Notice text : It is recommended to use an extruder equipped with
: a 25D or greater polyamide screw.It is also
: recommended to avoid high levels of shearing action.
: For extrusion of tubes, a calibration device should
: be used which has a conical entry and good
: regulation of cooling water flow.
Chemical Media Resistance
| Acids | |
 | Sulfuric Acid (5% by mass) (23°C) |
| Bases | |
| Sodium Hydroxide solution (1% by mass) (23°C) |
| Alcohols | |
| Methanol (23°C) |
| Ethanol (23°C) |
| Hydrocarbons | |
| Toluene (23°C) |
| Ketones | |
| Acetone (23°C) |
| Standard Fuels | |
| Standard fuel with alcohol (pref. ISO 1817 Liquid 4) (23°C) |
| Salt solutions | |
| Zinc Chloride solution (50% by mass) (23°C) |
Disclaimer
This database provides the main properties of technical thermoplastics
marketed by ARKEMA.
The information contained in this document is based on trials carried
out by our Research Centres and data selected from the literature, but
shall in no event be held to constitute or imply any warranty,
undertaking, express or implied commitment from our part.
Our format specifications define the limit of our commitment.
No liability whatsoever can be accepted by ARKEMA with regard to the
handling processing or use of the product or products concerned which
much in all cases be employed in accordance with all relevant laws
and/or regulations in force in the country or countries concerned.
For information about the other products marketed
by our company consult :
ARKEMAGROUP.COM
The CAMPUS internet database is hosted by M-Base Engineering + Software GmbH.
M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors.
Any decision about the application of materials must be double checked with the producer of this material.
CAMPUS® is a Registered trademark of CWFG mbH, Frankfurt/Main, 1991
CAMPUS® is a Registered trademark of CWFG mbH, Frankfurt/Main, 1991