CAMPUS® datasheet | ORGALLOY LT 4060


This datasheet of ORGALLOY LT 4060 from ARKEMA is provided by the international plastics database CAMPUS.

CAMPUS is organized by a group of leading international resin producers, who have agreed to test their material according to uniform conditions, based on ISO standards (ISO 10350, ISO 11403), in order to offer comparable data to the market.

This datasheet includes:
Rheological properties - Mechanical properties - Thermal properties - Electrical properties - Other properties - Test specimen production - Diagrams
  ORGALLOY LT 4060 | PA6... | ARKEMA
Product Texts
ORGALLOY LT 4060 - LT 4060ES NOIR T6L 

Very flexible polyamide alloys: easy to process, low moisture 
absorption, good mechanical properties at low temperature. Demonstrate a 
good balance of properties eg, high flexibility (200 MPa), good thermal 
performance and and ductility at low temperatures.

LT 4060    : standard grade, injection moulding or tubes, mandrels...

LT 4060ES NOIR T6L  : blow moulding grade or tube extrusion.
top
Rheological propertiesdry / condUnitTest Standard
Melt volume-flow rate (MVR) 1.7 / * cm³/10min ISO 1133
Temperature 235 / * °C ISO 1133
Load 5 / * kg ISO 1133
Molding shrinkage (parallel) 0.7 / * % ISO 294-4, 2577
Molding shrinkage (normal) 0.9 / * % ISO 294-4, 2577
top
Mechanical propertiesdry / condUnitTest Standard
Tensile Modulus - / 300 MPa ISO 527-1/-2
Stress at 50% strain - / 22 MPa ISO 527-1/-2
Strain at break - / >50 % ISO 527-1/-2
Charpy impact strength (+23°C) N / N kJ/m² ISO 179/1eU
Charpy notched impact strength (+23°C) N / N kJ/m² ISO 179/1eA
Charpy notched impact strength (-30°C) - / 22 kJ/m² ISO 179/1eA
top
Thermal propertiesdry / condUnitTest Standard
Melting temperature (10°C/min) 220 / * °C ISO 11357-1/-3
Temp. of deflection under load (0.45 MPa) 60 / * °C ISO 75-1/-2
Burning Behav. at 1.5 mm nom. thickn. HB / * class IEC 60695-11-10
Thickness tested 1.6 / * mm IEC 60695-11-10
Burning Behav. at thickness h HB / * class IEC 60695-11-10
Thickness tested 3.2 / * mm IEC 60695-11-10
top
Electrical propertiesdry / condUnitTest Standard
Comparative tracking index * / 600 - IEC 60112
top
Other propertiesdry / condUnitTest Standard
Water absorption 5 / * % Sim. to ISO 62
Humidity absorption 1.1 / * % Sim. to ISO 62
Density 1040 / 1040 kg/m³ ISO 1183
top
Test specimen productionValueUnitTest Standard
Injection Molding, melt temperature 260 °C ISO 294
Injection Molding, mold temperature 60 °C ISO 10724
top
Diagrams
Dynamic Shear modulus-temperature , ORGALLOY LT 4060, PA6..., ARKEMA
Stress-strain , ORGALLOY LT 4060, PA6..., ARKEMA
Secant modulus-strain , ORGALLOY LT 4060, PA6..., ARKEMA
top
Characteristics
Processing
Injection Molding, Profile Extrusion, Other Extrusion, Transfer Molding
Delivery form
Pellets
Special Characteristics
Platable, Light stabilized or stable to light, Heat stabilized or stable to heat
Regional Availability
North America, Europe, Asia Pacific, South and Central America, Near East/Africa
top
Other text information
Injection molding
PREPROCESSING
 

Max water content:      0,05-0,15       %

Notice text      :      ORGALLOY grades are delivered ready for use. 
   
                 :      If Orgalloy is not used within 4 hours of opening
                 :      the bag,the product should be redried at 90°C
                 :      during 4 hours.

PROCESSING

Melt temperature :      240-280 °C
Mold temperature :       40- 80 °C

Notice text      :      To avoid degradation, it is recommended to limit
                 :      injection moulding temperature to 300°C.

                 :      A higher mould temperature leads to higher shrinkage..

POSTPROCESSING

Annealing

-Temperature     :      80-120  °C
-Time            :      0,5 - 1 h

Notice text      :      Post treatment enables optimum dimensional 
                 :      stability.The treatment temperature is function
                 :      of the temperature towhich the part will experience.

                 :      ORGALLOY grades have low sensitivity to humidity.
                 :      Therefore it is not normally necessary to
                 :      precondition prior to assembly.
Profile extrusion
PREPROCESSING


Max water content:      0,05-0,15       %

Notice text      :      ORGALLOY grades are delivered ready for use. 
   
                 :      If Orgalloy is not used within 4 hours of opening
                 :      the bag,the product should be redried at 90°C
                 :      during 4 hours.

PROCESSING
     

Melt temperature :      255-265 °C


Notice text      :      It is recommended to use an extruder equipped with 
                 :      a 25D or greater polyamide screw.It is also
                 :      recommended to avoid high levels of shearing action.

                 :      For extrusion of tubes, a calibration device should
                 :      be used which has a conical entry and good
                 :      regulation of cooling water flow.
top
Chemical Media Resistance
Acids
Sulfuric Acid (5% by mass) (23°C)
Bases
Sodium Hydroxide solution (1% by mass) (23°C)
Hydrocarbons
Toluene (23°C)
Ketones
Acetone (23°C)
Salt solutions
Zinc Chloride solution (50% by mass) (23°C)
Other
Ethylene Glycol (50% by mass) in water (108°C)
top
Disclaimer

This database provides the main properties of technical thermoplastics
marketed by ARKEMA.

      The information contained in this document is based on trials carried
out by our Research Centres and data selected from the literature, but
shall in no event be held to constitute or imply any warranty,
undertaking, express or implied commitment from our part.
Our format specifications define the limit of our commitment.
No liability whatsoever can be accepted by ARKEMA with regard to the
handling processing or use of the product or products concerned which
much in all cases be employed in accordance with all relevant laws
and/or regulations in force in the country or countries concerned.

For information about the other products marketed
by our company consult :