CAMPUS® datasheet | Pocan® KU 2-7604


This datasheet of Pocan® KU 2-7604 from LANXESS Deutschland GmbH is provided by the international plastics database CAMPUS.

CAMPUS is organized by a group of leading international resin producers, who have agreed to test their material according to uniform conditions, based on ISO standards (ISO 10350, ISO 11403), in order to offer comparable data to the market.

This datasheet includes:
Rheological properties - Mechanical properties - Thermal properties - Other properties - Test specimen production
  Pocan® KU 2-7604 | (PBT+PC) FR | LANXESS Deutschland GmbH
Product Texts
PBT+PC, non-reinforced, injection moulding, extrusion, flame retardant, impact modified, low tendency to warp
top
Rheological propertiesValueUnitTest Standard
Melt volume-flow rate (MVR) 10 cm³/10min ISO 1133
Temperature 260 °C ISO 1133
Load 5 kg ISO 1133
Molding shrinkage (parallel) 0.8 % ISO 294-4, 2577
Molding shrinkage (normal) 0.9 % ISO 294-4, 2577
top
Mechanical propertiesValueUnitTest Standard
Tensile Modulus 2000 MPa ISO 527-1/-2
Yield stress 45 MPa ISO 527-1/-2
Yield strain 3.5 % ISO 527-1/-2
Nominal strain at break 14 % ISO 527-1/-2
Charpy impact strength (+23°C) N kJ/m² ISO 179/1eU
Charpy impact strength (-30°C) N kJ/m² ISO 179/1eU
top
Thermal propertiesValueUnitTest Standard
Melting temperature (10°C/min) 225 °C ISO 11357-1/-3
Temp. of deflection under load (1.80 MPa) 80 °C ISO 75-1/-2
Temp. of deflection under load (0.45 MPa) 102 °C ISO 75-1/-2
Coeff. of linear therm. expansion (parallel) 100 E-6/K ISO 11359-1/-2
Coeff. of linear therm. expansion (normal) 110 E-6/K ISO 11359-1/-2
Burning Behav. at thickness h V-0 class IEC 60695-11-10
Thickness tested 0.8 mm IEC 60695-11-10
top
Other propertiesValueUnitTest Standard
Water absorption 0.3 % Sim. to ISO 62
Humidity absorption 0.1 % Sim. to ISO 62
Density 1300 kg/m³ ISO 1183
top
Test specimen productionValueUnitTest Standard
Injection Molding, melt temperature 260 °C ISO 294
Injection Molding, mold temperature 80 °C ISO 10724
top
Characteristics
Processing
Injection Molding
Delivery form
Pellets
Regional Availability
North America, Europe, Asia Pacific, South and Central America, Near East/Africa
top
Other text information
Injection molding
PREPROCESSING
Max. Water content: 0.04 %
Drying temperature: 120 °C

Drying time:
Circulating air drying oven (50 % fresh air) 4-8 h
Fresh air dryer (high speed dryer) 2-3 h
Dry air dryer 2-3 h

PROCESSING
Melt temperature: 240 - 260 °C
Mold temperature: 80 - 100 °C
top
Disclaimer
This information and our  technical advice - whether verbal, in  writing
or by way of trials - are  given in good faith but without warranty, and
this  also  applies  where  proprietary  rights  of  third  parties  are
involved.  Our advice does not release you from  the obligation to check
its validity and to test our  products  as to their  suitability for the
intended processes and uses.  The  application, use  and  processing  of
our products and the products manufactured  by  you  on the basis of our
technical  advice  are  beyond our control and, therefore, entirely your
own  responsibility.  Our  products  are  sold  in  accordance  with our
General  Conditions of Sale and Delivery.
The values  stored in the databank should only be used as guidelines for
component   design.  In  giving  these  values  neither  guarantee,  nor
assurance of particular material properties can be given.