CAMPUS® datasheet | RADIFLAM® A RV250FR


This datasheet of RADIFLAM® A RV250FR from RadiciPlastics is provided by the international plastics database CAMPUS.

You may contact the supplier for more information about this grade.

This datasheet includes:
Mechanical properties - Thermal properties - Electrical properties - Other properties - Test specimen production - Diagrams
  RADIFLAM® A RV250FR | PA66-GF25 FR | RadiciPlastics
Product Texts
DESIGNATION:
Thermoplastics ISO1874-PA66,MFR,-140,GF25

BRIEF DESCRIPTION:
PA66 Flame retardant injection moulding grade
halogens or phosphorus free.
25% Glass fibre reinforced.
For high stiffness items. Good dimensional stability
UL94 V0 rated
top
Mechanical propertiesdry / condUnitTest Standard
Tensile Modulus 14000 / - MPa ISO 527-1/-2
Stress at break 155 / - MPa ISO 527-1/-2
Strain at break 2.3 / - % ISO 527-1/-2
Charpy impact strength, +23°C 40 / - kJ/m² ISO 179/1eU
Charpy impact strength, -30°C 30 / - kJ/m² ISO 179/1eU
Charpy notched impact strength, +23°C 4.2 / - kJ/m² ISO 179/1eA
Charpy notched impact strength, -30°C 3.8 / - kJ/m² ISO 179/1eA
top
Thermal propertiesdry / condUnitTest Standard
Melting temperature, 10°C/min 260 / * °C ISO 11357-1/-3
Temp. of deflection under load, 1.80 MPa 210 / * °C ISO 75-1/-2
Temp. of deflection under load, 0.45 MPa 220 / * °C ISO 75-1/-2
Vicat softening temperature, 50°C/h 50N 220 / * °C ISO 306
Burning Behav. at 1.5 mm nom. thickn. V-0 / * class IEC 60695-11-10
Thickness tested 1.6 / * mm IEC 60695-11-10
UL recognition UL / * - -
Burning Behav. at thickness h V-0 / * class IEC 60695-11-10
Thickness tested 0.8 / * mm IEC 60695-11-10
top
Electrical propertiesdry / condUnitTest Standard
Volume resistivity >1E13 / 1E13 Ohm*m IEC 60093
Surface resistivity * / 1E14 Ohm IEC 60093
Comparative tracking index * / 600 - IEC 60112
top
Other propertiesdry / condUnitTest Standard
Water absorption 2.4 / * % Sim. to ISO 62
Humidity absorption 0.9 / * % Sim. to ISO 62
Density 1680 / * kg/m³ ISO 1183
top
Test specimen productionValueUnitTest Standard
Processing conditions acc. ISO 1870 - ISO ....-2
Injection Molding, melt temperature 290 °C ISO 294
Injection Molding, mold temperature 80 °C ISO 10724
top
Diagrams
Stress-strain , RADIFLAM® A RV250FR, PA66-GF25 FR, RadiciPlastics
Secant modulus-strain , RADIFLAM® A RV250FR, PA66-GF25 FR, RadiciPlastics
top
Characteristics
Processing
Injection Molding
Delivery form
Pellets
Additives
Lubricants
Regional Availability
North America, Europe, Asia Pacific, South and Central America, Near East/Africa
top
Other text information
Injection molding
PREPROCESSING
Max. water content 0.2%
Drying temperature 80°C
Drying time 2-4h (dry air dryer)

PROCESSING
Melt temperature 290°C
Mold temperature 80°C
top
Disclaimer
This database provides the technical properties
of thermoplastics produced and marketed by
RADICI NOVACIPS
and his subsidiaries companies:

RADILON® A          Polyamide 66
RADILON® S          Polyamide 6
RADILON® CA       Copolyamide 66/6
RADILON® CS       Copolyamide 6 semiaromatic
RADITER® B          Poly(butylene terephthalate)
RADIFLAM® A         Polyamide 66,  self-extinguishing
RADIFLAM® S         Polyamide 6,   self-extinguishing
RADIFLAM® B         Polybutylene terephthalate, self-extinguishing
HERAFLEX® A        Stirenic Thermoplastic Elastomer SEBS
HERAFLEX® E        Ether-Ester Thermoplastic Elastomer
HERAFLEX® B        Stirenic Thermoplastic Elastomer SBS
HERAFLEX® P        Modified Polypropylene
RADILENE® R        Polyethylene and Polypropylene

The data and graphs contained in this database were carried out
by our Research Centers and shall in no event be held to
constitute or imply any warranty, undertaking, express or
implied commitment from our part.
top

The CAMPUS internet database is hosted by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

CAMPUS® is a registered trademark of CWFG mbH, Frankfurt am Main, 2012