CAMPUS® datasheet | SCHULAMID® 6 MV HI


This datasheet of SCHULAMID® 6 MV HI from A. Schulman GmbH is provided by the international plastics database CAMPUS.

CAMPUS is organized by a group of leading international resin producers, who have agreed to test their material according to uniform conditions, based on ISO standards (ISO 10350, ISO 11403), in order to offer comparable data to the market.

You may contact the supplier for more information about this grade.

This datasheet includes:
Rheological properties - Mechanical properties - Thermal properties - Electrical properties - Other properties - Rheological calculation properties - Test specimen production - Diagrams
  SCHULAMID® 6 MV HI | PA6-I | A. Schulman GmbH
Product Texts
Increased impact modified PA 6 standard grade


top
Rheological propertiesdry / condUnitTest Standard
Molding shrinkage (parallel) 1.1 / * % ISO 294-4, 2577
top
Mechanical propertiesdry / condUnitTest Standard
Tensile Modulus 2600 / 1000 MPa ISO 527-1/-2
Yield stress 74 / 43 MPa ISO 527-1/-2
Yield strain 4.2 / 20 % ISO 527-1/-2
Nominal strain at break >50 / >50 % ISO 527-1/-2
Charpy impact strength (+23°C) N / N kJ/m² ISO 179/1eU
Charpy impact strength (-30°C) N / N kJ/m² ISO 179/1eU
Charpy notched impact strength (+23°C) 15 / 50 kJ/m² ISO 179/1eA
Charpy notched impact strength (-30°C) 8 / 12 kJ/m² ISO 179/1eA
top
Thermal propertiesdry / condUnitTest Standard
Melting temperature (10°C/min) 219 / * °C ISO 11357-1/-3
Glass transition temperature (10°C/min) 40 / * °C ISO 11357-1/-2
Temp. of deflection under load (1.80 MPa) 70 / * °C ISO 75-1/-2
Temp. of deflection under load (0.45 MPa) 190 / * °C ISO 75-1/-2
Vicat softening temperature (50°C/h 50N) 195 / * °C ISO 306
Burning Behav. at 1.5 mm nom. thickn. HB / * class IEC 60695-11-10
Thickness tested 1.5 / * mm IEC 60695-11-10
UL recognition UL / * - -
top
Electrical propertiesdry / condUnitTest Standard
Relative permittivity (100Hz) 3.5 / 12 - IEC 60250
Relative permittivity (1MHz) 3.3 / 4.4 - IEC 60250
Dissipation factor (100Hz) 0.011 / 0.14 E-4 IEC 60250
Dissipation factor (1MHz) 0.019 / 0.09 E-4 IEC 60250
Volume resistivity >1E13 / 1E10 Ohm*m IEC 60093
Surface resistivity * / >1E15 Ohm IEC 60093
Comparative tracking index - / 600 - IEC 60112
top
Other propertiesdry / condUnitTest Standard
Humidity absorption 2.3 / * % Sim. to ISO 62
Density 1110 / - kg/m³ ISO 1183
top
Rheological calculation propertiesValueUnitTest Standard
Density of melt 935 kg/m³ -
Thermal conductivity of melt 0.25 W/(m K) -
Spec. heat capacity melt 1600 J/(kg K) -
Eff. thermal diffusivity 8E-8 m²/s -
Ejection temperature 110 °C -
top
Test specimen productionValueUnitTest Standard
Processing conditions acc. ISO 1870 - ISO ....-2
Injection Molding, melt temperature 250 °C ISO 294
Injection Molding, mold temperature 80 °C ISO 10724
Injection Molding, injection velocity 250 mm/s ISO 294
Injection Molding, pressure at hold 70 MPa ISO 294
top
Diagrams
Viscosity-shear rate , SCHULAMID® 6 MV HI, PA6-I, A. Schulman
Shearstress-shear rate , SCHULAMID® 6 MV HI, PA6-I, A. Schulman
top
Characteristics
Processing
Injection Molding
Delivery form
Granules
Additives
Release agent, Plasticizer
Regional Availability
North America, Europe, Asia Pacific, South and Central America, Near East/Africa
top
Other text information
Injection molding
Pretreatment
Predrying: 4-6h / 80°C

Processing:

Melttemperature250 - 270°C
Mouldtemperature60 - 90°C

top
Disclaimer
The properties given in this software are typical, non-binding
mean values found fpor injection moulded natural coloured test
bars. Pigments and other modification may alter these values.
The characteristic values are based on our know-how and experience.
They do not warrant any specific properties. All our products
must be subjected to in house tests and inspections by the user
before application. This applies above all with regard to their
suitability for a particular purpose. It also applies accordingly
for all other written or verbal information given by our personnel.
Our General Terms of Business apply in all other respects,
particulaly with regard to liability for material defects.

If there are questions to given information, to further
properties or further A. Schulman products please contact

                  A. Schulman GmbH
                  Huettenstrasse 211
                  50170 Kerpen
                  Tel: 02273 / 561-0
                  Contact: Dipl.-Ing. M. Berg
                           aschulman@de.aschulman.com
                           Subject: Material data
top