offers extended functionality!CAMPUS® datasheet | VESTAMID EX9350 blk (sw)
This datasheet of VESTAMID EX9350 blk (sw) from Evonik Industries AG is provided by the international plastics database CAMPUS.
CAMPUS is organized by a group of leading international resin producers, who have agreed to test their material according to uniform conditions, based on ISO standards (ISO 10350, ISO 11403), in order to offer comparable data to the market.
Heat- and weather-resistant, impact-modified polyamide 612 elastomer for extrusion
Resin: ISO 1874-PA612-PPGD,EHL,18-005
VESTAMID® EX9350 is a PA 612 elastomer extrusion compound developed for the manufacturing
of tubing systems, e.g. vacuum brake booster lines.
The compound is in particular suitable for applications, that require a continuous high flexibility
even if subjected to high temperature load. In contrast to conventionally plasticized materials
(plasticizerloss) tubes made from VESTAMID® EX9350 do not stiffen under elevated temperatures.
The compound is especially suitable for the extrusion of tubing systems that are exposed to in-
creased burst pressures and service temperatures.
| Rheological properties | dry / cond | Unit | Test Standard |
| Molding shrinkage (parallel) | 1.1 / * | % | ISO 294-4, 2577 |
| Molding shrinkage (normal) | 1.0 / * | % | ISO 294-4, 2577 |
| Mechanical properties | dry / cond | Unit | Test Standard | ||||||||||||||||||||||||||||
| Tensile Modulus | 600 / - | MPa | ISO 527-1/-2 | ||||||||||||||||||||||||||||
| Yield stress | 30 / - | MPa | ISO 527-1/-2 | ||||||||||||||||||||||||||||
| Yield strain | 35 / - | % | ISO 527-1/-2 | ||||||||||||||||||||||||||||
| Nominal strain at break | >50 / - | % | ISO 527-1/-2 | ||||||||||||||||||||||||||||
| Charpy impact strength (+23°C) | N / - | kJ/m² | ISO 179/1eU | ||||||||||||||||||||||||||||
| Charpy impact strength (-30°C) | N / - | kJ/m² | ISO 179/1eU | ||||||||||||||||||||||||||||
| Charpy notched impact strength (+23°C) | 110[P] / - | kJ/m² | ISO 179/1eA | ||||||||||||||||||||||||||||
| Charpy notched impact strength (-30°C) | 8 / - | kJ/m² | ISO 179/1eA | ||||||||||||||||||||||||||||
| |||||||||||||||||||||||||||||||
| Thermal properties | dry / cond | Unit | Test Standard |
| Melting temperature (10°C/min) | 198 / * | °C | ISO 11357-1/-3 |
| Temp. of deflection under load (1.80 MPa) | 50 / * | °C | ISO 75-1/-2 |
| Temp. of deflection under load (0.45 MPa) | 130 / * | °C | ISO 75-1/-2 |
| Vicat softening temperature (50°C/h 50N) | 130 / * | °C | ISO 306 |
| Other properties | dry / cond | Unit | Test Standard |
| Water absorption | 1.1 / * | % | Sim. to ISO 62 |
| Humidity absorption | 3.5 / * | % | Sim. to ISO 62 |
| Density | 1050 / - | kg/m³ | ISO 1183 |
PREPROCESSING INFORMATION
Maximum Water Content: 0.1 %
When the indicated water content is exceeded, the resin must be dried. The drying time is dependent
on the drying temperature. At a drying temperature of 80 °C we recommend, depending on the water
content, a drying time of 8 - 16 hours. Fresh air dryers are acceptable, better would be a dry air or
vacuum dryer. Please note our product literature, plasticized resins can lose plasticizer during drying.
PROCESSING INFORMATION
Melt Temperature : 210 - 240 °C
With the following data, which reflect our current knowledge and experience, we wish to describe possible applications, however this information is given without guarantee or assurance of the appropriate properties for a specific application. The processor is not relieved of the responsibility for incoming quality control nor from his own testing and analysis. All data concerning product safety (EG-guideline, BGVV, FDA) are of principle nature and can be limitied regarding migration, temperature and type of food. They reflect the status as of Feb. 29, 2012. To insure that this data reflects the current state, please contact our Product Safety Department. Should you have any questions, wishes or suggestions about CAMPUS, please refer to the following address: Link to Evonik Industries AG homepage In any case, we hope you enjoy working with CAMPUS!