CAMPUS® datasheet | VESTORAN® X7342 nc (nf)
This datasheet of VESTORAN® X7342 nc (nf) from Evonik Industries AG is provided by the international plastics database CAMPUS.
VESTORAN® is the registered Evonik Degussa GmbH trademark for molding compounds containing
poly-2,6-dimethyl-1,4-phenylene ether as polymeric constituent (poly-phenylene ether, PPE, also
referred to as PPO).
As a material of amorphous structure, VESTORAN® X7342 shows very small mold shrinkage.
Therefore molded parts have a very low tendency to warp.
Moldings of VESTORAN® X7342 are dimensionally stable and hydrolysis resistant even in hot water,
but are more sensitive to organic solvents than semi-crystalline plastics. VESTORAN® X7342 is re-
sistant to aqueous alkalines and acides, certain alcohols, and glycol solutions. Due to the glass fiber
reinforcement the compound combines outstanding heat deflection temperature under load with high
strength and rigidity. The even smaller shrinkage compared to non-reinforced VESTORAN® depends on
the orientation of the glass fibers in the molded part.
| Rheological properties | Value | Unit | Test Standard |
| Melt volume-flow rate, MVR | 40 | cm³/10min | ISO 1133 |
| Temperature | 300 | °C | ISO 1133 |
| Load | 21.6 | kg | ISO 1133 |
| Mechanical properties | Value | Unit | Test Standard |
| Tensile Modulus | 5900 | MPa | ISO 527-1/-2 |
| Stress at break | 100 | MPa | ISO 527-1/-2 |
| Strain at break | 2.5 | % | ISO 527-1/-2 |
| Charpy impact strength, +23°C | 45 | kJ/m² | ISO 179/1eU |
| Charpy notched impact strength, +23°C | 14 | kJ/m² | ISO 179/1eA |
| Thermal properties | Value | Unit | Test Standard |
| Temp. of deflection under load, 1.80 MPa | 165 | °C | ISO 75-1/-2 |
| Temp. of deflection under load, 0.45 MPa | 170 | °C | ISO 75-1/-2 |
| Vicat softening temperature, 50°C/h 50N | 170 | °C | ISO 306 |
| Coeff. of linear therm. expansion, parallel | 40 | E-6/K | ISO 11359-1/-2 |
| Coeff. of linear therm. expansion, normal | 30 | E-6/K | ISO 11359-1/-2 |
| Burning Behav. at 1.5 mm nom. thickn. | HB | class | IEC 60695-11-10 |
| Thickness tested | 1.6 | mm | IEC 60695-11-10 |
| Burning Behav. at thickness h | HB | class | IEC 60695-11-10 |
| Thickness tested | 0.8 | mm | IEC 60695-11-10 |
| UL recognition | UL | - | - |
| Electrical properties | Value | Unit | Test Standard |
| Relative permittivity, 100Hz | 3 | - | IEC 60250 |
| Relative permittivity, 1MHz | 3.5 | - | IEC 60250 |
| Dissipation factor, 100Hz | 80 | E-4 | IEC 60250 |
| Dissipation factor, 1MHz | 10 | E-4 | IEC 60250 |
| Volume resistivity | >1E13 | Ohm*m | IEC 60093 |
| Comparative tracking index | 175 | - | IEC 60112 |
| Other properties | Value | Unit | Test Standard |
| Density | 1190 | kg/m³ | ISO 1183 |
| Rheological calculation properties | Value | Unit | Test Standard |
| Density of melt | 1010 | kg/m³ | - |
| Thermal conductivity of melt | 0.25 | W/(m K) | - |
| Spec. heat capacity of melt | 1640 | J/(kg K) | - |
| Test specimen production | Value | Unit | Test Standard |
| Injection Molding, melt temperature | 320 | °C | ISO 294 |
| Injection Molding, mold temperature | 80 | °C | ISO 10724 |
| Injection Molding, injection velocity | 200 | mm/s | ISO 294 |
PREPROCESSING INFORMATION
Maximum Water Content: 0.1 %
If the given water content is exceeded or silver streaks appear on the surface of parts, the resin should be dried.
Drying should be carried out is a dry air or vacuum dryer for at least 3 to 4 hours at 90 - 120°C. The resin should
be pre-heated to 80 - 110°C before molding. If a vented plastizier zone employed preheating can be omitted.
Please refer to our product information sheets!
PROCESSING INFORMATION
| Melt Temperature: | 280 - 310 | °C |
| Mold Temperature: | 60 - 100 | °C |
All listed technical data are typical values intended for your guidance.
They are given without obligation and do not constitute a materials
specification. Should you have any further questions concerning material
behavior or properties, please contact us at the following address :
for PA: Evonik Industries AG
PP-HP-CRM
Gebäude 1227 / PB 16
D-45764 Marl
Phone: +49-(0)2365/49-2720
Fax:+49-(0)2365/49-2070
E-Mail: campusplastics@evonik.com
for PMMA: Evonik Industries AG
Marketing / Campus
Kirschenallee
D-64293 Darmstadt
Germany
Phone: +49 - (0) 61 51 / 18-47 11
Fax: +49 - (0) 61 51 / 18-31 77
E-Mail: campusplastics@evonik.com
Internet: http://www.plexiglas-polymers.com
® = registered trademark
PLEXIGLAS® is a registered trademark of Evonik Röhm GmbH, Germany,
outside of the Americas. Within the Americas it is sold as ACRYLITE®,
which is a registered trademark of Evonik Cyro LLC, USA.
PLEXIMID® is a registered trademarks of Evonik Röhm GmbH, Germany.
CYROLITE® and XT® polymer are registered trademarks of Evonik Cyro LLC, USA.
This information and all further technical advice is based on our present knowledge
and experience. However, it implies no liability or other legal responsibility on our part,
including with regard to existing third party intellectual property rights, especially
patent rights. In particular, no warranty, whether express or implied, or guarantee of
product properties in the legal sense is intended or implied. We reserve the right to
make any changes according to technological progress or further developments. The
customer is not released from the obligation to conduct careful inspection and testing
of incoming goods. Performance of the product described herein should be verified by
testing, which should be carried out only by qualified experts in the sole responsibility
of a customer. Reference to trade names used by other companies is neither a
recommendation, nor does it imply that similar products could not be used.
NAFTA:
This information and all technical and other advice are based on Evonik’s
present knowledge and experience. However, Evonik assumes no liability for
such information or advice, including the extent to which such information or
advice may relate to third party intellectual property rights. Evonik reserves the
right to make any changes to information or advice at any time, without prior
or subsequent notice. EVONIK DISCLAIMS ALL REPRESENTATIONS AND
WARRANTIES, WHETHER EXPRESS OR IMPLIED, AND SHALL HAVE NO LIABILITY
FOR, MERCHANTABILITY OF THE PRODUCT OR ITS FITNESS FOR A PARTICULAR
PURPOSE (EVEN IF EVONIK IS AWARE OF SUCH PURPOSE), OR OTHERWISE.
EVONIK SHALL NOT BE RESPONSIBLE FOR CONSEQUENTIAL, INDIRECT OR
INCIDENTAL DAMAGES (INCLUDING LOSS OF PROFITS) OF ANY KIND. It is the
customer’s sole responsibility to arrange for inspection and testing of all
products by qualified experts. Reference to trade names used by other
companies is neither a recommendation nor an endorsement of the
corresponding product, and does not imply that similar products could not be
used.
Sales range and technical data subject to alteration.
CAMPUS® is a registered trademark of CWFG mbH, Frankfurt am Main, 2012