CAMPUS® datasheet | BERGAMID® B70MI20
This datasheet of BERGAMID® B70MI20 from PolyOne Engineered Materials Europe is provided by the international plastics database CAMPUS.
BERGAMID® B70MI20 | PA6-MD20 | PolyOne Engineered Materials Europe
제품 설명서
BERGAMID B70MI20, PA6 reinforced
general-purpose injection molding grade
20% minerals
general-purpose injection molding grade
20% minerals
| 기계적 특성 | 건조/응축 | 단위 | 시험규격 |
| 인장탄성률 | 4000 / 1700 | MPa | ISO 527-1/-2 |
| 파단시 강도 | 75 / 40 | MPa | ISO 527-1/-2 |
| 파단시 신율 | 19 / 50 | % | ISO 527-1/-2 |
| 챠피 충격 강도 , +23°C | N / N | kJ/m² | ISO 179/1eU |
| 챠피 노치드 충격 강도, +23°C | 9 / 20 | kJ/m² | ISO 179/1eA |
| 챠피 노치드 충격 강도, -30°C | 7 / - | kJ/m² | ISO 179/1eA |
| 열적 특성 | 건조/응축 | 단위 | 시험규격 |
| 녹는점, 10°C/min | 223 / * | °C | ISO 11357-1/-3 |
| 하중하에서의 변형온도, 1.80 MPa | 60 / * | °C | ISO 75-1/-2 |
| 하중하에서의 변형온도, 0.45 MPa | 190 / * | °C | ISO 75-1/-2 |
| 1.5mm 평균두께에서의 난연성 | HB / * | class | IEC 60695-11-10 |
| 테스트 두께 | 1.6 / * | mm | IEC 60695-11-10 |
| 두께 H인 제품의 난연성 | HB / * | class | IEC 60695-11-10 |
| 테스트 두께 | 0.8 / * | mm | IEC 60695-11-10 |
| 전기적 특성 | 건조/응축 | 단위 | 시험규격 |
| 상대 유전뮬, 1MHz | 3.8 / 6.2 | - | IEC 60250 |
| 소산 인자, 1MHz | 200 / 2000 | E-4 | IEC 60250 |
| 부피 저항 | 1E13 / 1E10 | Ohm*m | IEC 60093 |
| 표면 저항 | * / 1E10 | Ohm | IEC 60093 |
| CTI | - / 500 | - | IEC 60112 |
| 물질의 비성질 | 건조/응축 | 단위 | 시험규격 |
| 점도수 | 150 / * | cm³/g | ISO 307, 1157, 1628 |
| 테스트 견본 생산 | 값 | 단위 | 시험규격 |
| 사출성형: 용융수지온도 | 270 | °C | ISO 294 |
| 사출성형: 금형온도 | 80 | °C | ISO 10724 |
특징
생산 공정
사출 성형
인도 유형
펠렛 (입자,알갱이)
지역별 검색
짱쨌쨈
화학적 매체에 대한 저항력
Disclaimer
PolyOnePolyOne Engineered Materials Europe
PolyOne Th.Bergmann GmbH
PolyOne Corporation makes no representations, guarantees or warranties of any kind with respect to the information contained in this document about its accuracy, suitability for particular applications ort he result obtained or obtainable using the information. Some of the information arises from laboratory work with small-case equipment which may not provide a reliable indication of performance or properties obtained or obtainable on larger-scale equipment. Processing conditions can cause material properties to shift from the values stated in data bases. PolyOne Corporation makes no guarantees or warranties respecting suitability of either PolyOne’s products or the information for your process or end-use application. You have the responsibility to conduct full-scale end-product performance testing to determine suitability in your application, and you assume all risks and liability arising from your use of the information and/or handling of any product. PolyOne Corporation makes no warranties, express or implied, including, but not limited to, implied warranties of merchantability and fitness for a particular purpose, either with respect to the information or products reflected by the information. These information shall not operate as permission, recommendation or inducement to practice any patented invention without permission of the patent owner.
Germany:
PolyOne Th.Bergmann GmbH
Adolf-Dambach-Strasse 2-4
D-76571 Gaggenau
Tel.: 07225 6802 0
Fax:07225 6802 10
France:
PolyOne Engineered Materials SA, FRANCE
20, Rue Salvador Allende, BP 105
42353 La Talaudière Cedex, France
Tel.: +33 (0) 477 47 64 00
Tel.:+33 (0) 477 57 13
Spain:
Pol. Ind. Valle del Cinca
22300 Barbastro, Spain
Tel.: +34 (0) 974 31 03 14
Fax.: +34 (0) 974 31 43 11
United Kingdom:
PolyOne Engineered Materials UL Ltd.
Newton Ayecliff
Durham DL5 6EA, UK
Tel.:+44 (0) 1325 30 08 48
Fax.:+44 (0) 1325 30 14 13
Turkey:
Tekno Polimer
103 Kücükcekmece
Istanbul, Turkey
Tel:+90 212 549 2256
Fax.:+90 212 549 2241
The CAMPUS internet database is hosted by M-Base Engineering + Software GmbH.
M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors.
Any decision about the application of materials must be double checked with the producer of this material.
CAMPUS® is a registered trademark of CWFG mbH, Frankfurt am Main, 2012
CAMPUS® is a registered trademark of CWFG mbH, Frankfurt am Main, 2012